For a better understanding of the hydrotalcite-like phase with SEM-EDS microanalysis, the present research paid special attention to the data acquisition and interpretation of this technique. A lower Mg/Al ratio was obtained when using a higher accelerating voltage, and a beam energy of 10 kV was more appropriate than 15 kV for investigation when the slag rim was thin, to compromise to meet the requirements of obtaining an adequate overvoltage ratio and minimizing the interference. Additionally, it was noted that the Mg/Al ratio decreased from zones rich in hydrotalcite-like phase to zones rich in the C−S−H gel phase, and indiscriminately fitting scatter points selected from the slag rim would bias the Mg/Al ratio of the hydrotalcite-like phase. According to the standard-based microanalysis, it was concluded that the analysis total of the hydrates within the slag rim was in the range of 30–40%, lower than that located in the cement matrix. Besides the water chemically bound in the C−S−H gel phase, the hydrotalcite-like phase also contained a certain amount of hydroxide ions and chemically bound water.@en

Because the essential quality metrics of blast furnace slag are based on its oxide composition, the determination of chemical compositions of unhydrated slag grains in an aged concrete could be useful for understanding its past performance and in predicting the remaining service life of existing slag-bearing concrete. In this research, the authors explored the feasibility of using standard-based energy-dispersive X-ray spectroscopy (EDS) microanalysis, in tandem with electron imaging, as a tool for quantitative measurement of the chemical composition of blast furnace slag grains in cement/concrete. In the experimental study, seven concrete samples representing various service life durations were collected in the Netherlands. The microanalysis results of the samples revealed that the change in slag chemistry is insignificant for samples B (1985) to F (2006); however, elevated CaO and SiO2 contents are found in slag used for sample G (2015), opposite to that of Al2O3 and MgO. After discussing compositional characterization, the paper discusses favorable microanalysis protocols for acceptable elemental quantification accuracy. It was concluded that quantitative EDS microanalysis is a strong tool to characterize the chemical composition of unhydrated slag used in field concrete, which could potentially contribute to understanding the correlations between composition and long-term performance in slag concrete structures.

@en