The internal temperature of proton exchange membrane fuel cells significantly influences their shutdown purge process a key factor for ensuring operational stability and longevity. This study explores how cell temperature impacts water removal mechanisms during shutdown purge, emphasizing its importance for the operational stability of fuel cell. High-temperature purge experiments were conducted using an integrated stack experimental platform, revealing that prolonged high-temperature purging increased the high frequency resistance of a single cell to 639.44 mΩ∙cm2 and caused severe perforation of the membrane electrode assembly. To delve deeper into the mechanisms of cell temperature influence and the cause of perforation, an isothermal, transient, two-phase flow fuel cell model was developed. The cell temperature during purge was incrementally raised from 303.15 K to 358.15 K in 5 K steps. Detailed analyses of membrane desorption and water phase changes during purge processes were performed. At cell temperatures ranging from 338.15 K to 358.15 K, a 120-s purge reduced the membrane water content to below 4.8, with only a 5 % variation in residual membrane water. When the cell temperature exceeded 323.15 K, water activity increased with temperature, intensifying evaporation and leading to desorption of vapor from the membrane. Consequently, higher temperatures facilitated the removal of liquid water, with no liquid water remaining within cell above 323.15 K. Elevated cell temperatures accelerated the purge, resulting in lower liquid water content and increased vapor, but with minimal difference in membrane water content. The intense evaporation process and rapid purge at high temperatures were identified as direct causes of membrane electrode assembly perforation. This study highlights the critical role of cell temperature in the shutdown purge process, providing innovative insights into optimizing proton exchange membrane fuel cell operations for enhanced performance and durability.@en

This paper comprehensively investigates the purge mechanism of proton exchange membrane fuel cells during the shutdown process, which qualitatively examines the effect of purge parameters (including current density, stoichiometric ratio, and relative humidity) on water content variation, and further quantitatively investigates the remaining water content post-purge. In contrast to previous studies, this paper offers a novel perspective on analyzing the purge process and conducts a thorough examination of residual water content. This study presents a transient, isothermal, two-phase flow model for proton exchange membrane fuel cells, which is subsequently validated experimentally. Results indicate that the significance of purge parameters follows the descending order: stoichiometric ratio, relative humidity, and current density. During the purge, the stoichiometric ratio should be rapidly increased to above 9. Each incremental rise in the stoichiometric ratio from 6 to 14 leads to a respective reduction in residual membrane water content after purge of 2.19 %, 1.57 %, 1.18 %, 0.93 %, 0.76 %, 0.63 %, 0.53 %, and 0.46 %. Similarly, it is recommended to swiftly decrease relative humidity to below 40 %. Elevating the purge current density from 20 to 200 mA/cm2 decreases the time required to completely remove liquid water from 20.24 s to 6.59 s. Hence, employing a higher current density at the onset of the purge facilitates quicker removal of liquid water, albeit resulting in an increase in residual membrane water content post-purge, from 3.17 to 3.70. In summary, optimizing the purge strategy requires adjusting purge current densities according to the specific purge stage.@en