Evaluation of low-cost oxygen carriers for biomass chemical looping gasification

Journal article (2023)

Authors

Avishek Goel Tampere University
Arnold Ismailov Tampere University
E. Mohammadzadeh Moghaddam Complex Fluid Processing - Mechanical, Maritime and Materials Engineering
Chao He Tampere University
Jukka Konttinen Tampere University
Research Group
Complex Fluid Processing (Mechanical, Maritime and Materials Engineering) (TU Delft)
Copyright: © 2023 Avishek Goel, Arnold Ismailov, E. Mohammadzadeh Moghaddam, Chao He, Jukka Konttinen
DOI: https://doi.org/10.1016/j.cej.2023.143948
More Info
expand_more

Published Date

2023

Language

English

Faculty

Mechanical, Maritime and Materials Engineering

Department

Process and Energy

Research Group

Complex Fluid Processing

Abstract

Biomass Chemical Looping Gasification (BCLG) is a cost-effective and efficient alternative to conventional gasification. The selection of appropriate oxygen carriers (OCs) is crucial for stable BCLG performance. These OCs need to possess high reactivity, selectivity, material strength, and resistance to sintering. The study investigated various OC materials, including industrial wastes (copper, nickel slag, desulphurization, LD, and ladle slags), residential waste (sewage sludge ash), and natural ore (manganese). The evaluation of OCs focused on reactivity, H2-selectivity, mechanical strength and sintering behaviour. Except for ladle slag, all OC samples exhibited favourable reactivity due to the presence of Fe- and Mn-oxides possessing high oxygen transport capacity (10–17.6%). Nickel slag, manganese ore, and desulphurisation slag displayed notable H2-selectivity (8.7 to 10.4). It can be attributed to the presence of less-active (lattice) oxygen, limiting strong oxygen agents such as Fe2O3, Fe3O4, and Mn2O3. Moreover, desulphurization slag contained highly selective Ca2Fe2O5, which falls within the partial oxidation zone of the Ellingham diagram. Furthermore, all OC samples exhibited desirable material strength (>20 MPa), suitable for fluidised bed reactors. However, nickel, LD, and ladle slags demonstrated limited sintering with sintering onset temperatures exceeding 963 °C. This limited sintering may be attributed to the absence of iron silicates, iron-bearing aluminium silicates, manganese silicates, and potassium that contributed to the low thermal stability observed in the remaining OCs. Altogether, nickel slag calcined at 1100 °C was identified as the most promising OC material with optimal reactivity, selectivity, material strength, and minimal sintering for BCLG. Overall, this study provides a detailed and scientific methodology for OC selection and can aid future OC development.