Can bi-functional nickel modified 13X and 5A zeolite catalysts for CO₂ methanation be improved by introducing ruthenium?

Abstract

Zeolites 13X and 5A were modified with nickel and/or ruthenium for CO₂ methanation. The catalysts were prepared by evaporation impregnation and XRD, SEM-EDX, TEM, STEM-EDX, nitrogen physisorption, H₂-TPR and NH₃-TPD were used to characterize the physico-chemical properties of the catalysts. The physico-chemical characterization results show that the zeolites structure did not change after the Ni, Ru modification, however. Ni was able to enter the pores of 13X, in the other case, 5A, an egg shell type structure was formed. Methanation experiments were performed in a lab scale fixed bed reactor system, the results showed that the mono-metallic catalysts out-performed the bi-metallic ones with Ni being the more active. One of the factors influencing the performance of the bi-metallic catalysts was the difficulty to obtain good dispersion when both metals were used. Also the morphology of the catalyst significantly influenced the selectivity. The catalysts with lower weak acidity benefit for getting a higher activity. The single metal catalysts 2.5 %Ru13X and 5%Ni13X showed good catalytic stability with around 97 % CH₄ selectivity at 360 °C, with no catalyst deactivation during the 200 h catalyst stability test.