Effect of different grade levels of calcined clays on fresh and hardened properties of ternary-blended cementitious materials for 3D printing

Abstract

This study aims to investigate the influences of different grades of calcined clay on 3D printability, compressive strength (7 days), and hydration of limestone and calcined clay-based cementitious materials. Calcined clays that contained various amounts of metakaolin were achieved by blending low-grade calcined clay (LGCC) and high-grade calcined clay (HGCC) in three different proportions. The results revealed that increasing the HGCC% ranging from 0 wt% to 50 wt% in calcined clay could: (1) increase the flow consistency; (2) impressively improve the buildability, and reduce the printability window of the fresh mixtures; (3) enhance and accelerate the cement hydration. The reduction of mean interparticle distance induced by increasing HGCC% may be the primary reason for the enhancement of buildability and very early-age hydration. However, increasing HGCC% led to an increase of air void content in the interface region of the printed sample, which weakened the compressive strength of the printed sample at 7 days. Besides, it confirmed that the cold-joint/weak interface was easily formed by using the fresh mixture with a high structuration rate.