Utilization of miscanthus combustion ash as internal curing agent in cement-based materials

Effect on autogenous shrinkage

Journal article (2019)

Authors

Yang Lv Universiteit Gent, Wuhan University of Technology
G. (Guang) Ye Materials and Environment - CEG , Universiteit Gent
Geert De Schutter Universiteit Gent
Research Group
Materials and Environment (CEG) (TU Delft)
More Info
expand_more

Published Date

2019

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Civil Engineering & Geosciences

Department

Materials- Mechanics- Management & Design

Research Group

Materials and Environment

Abstract

The present study aims to evaluate the characterization of combustion ash of miscanthus and its possible application for self-desiccation and autogenous shrinkage mitigation in cement-based materials. Comprehensive tests were performed on the sealed samples to evaluate the behavior of self-desiccation and autogenous shrinkage of low water/binder ratio (0.25) cement pastes blended with miscanthus ash (MA). The lab-generated MA is featured by high content of amorphous silica and porous structure. Its porous structure with pore size distribution mainly within the range of 30–50 nm in diameter makes it a potential internal curing agent for self-desiccation and autogenous shrinkage mitigation. Incorporation of 20% by weight MA into cement paste shows high efficiency in self-desiccation mitigation, contributing to the significantly reduced autogenous shrinkage. Decreasing the mean particle size from 20.43 µm to 6.67 µm lowers the self-desiccation mitigation efficiency of biomass ash MA in the blended cement pastes.