Enhancing shape memory properties of multi-layered and multi-material polymer composites in 4D printing

Journal article (2021)

Authors

Nima Roudbarian University of Tehran
Mahdi Baniasadi University of Tehran
Pooyan Nayyeri Toronto Metropolitan University
Mahdi Ansari Arak University of Technology
R. Hedayati Novel Aerospace Materials - Aerospace Engineering
Mostafa Baghani University of Tehran
Research Group
Novel Aerospace Materials (Aerospace Engineering) (TU Delft)
More Info
expand_more

Published Date

2021

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Aerospace Engineering

Department

Aerospace Structures & Materials

Research Group

Novel Aerospace Materials

Abstract

The shape memory behavior of smart materials is widely used for stimulation or shape-shifting purposes. Shape memory polymers (SMPs) can shape and force recoveries accompanied by attractive attributes such as biocompatibility, biodegradability, and universality. In this paper, a thermoplastic elastomer (TPE) is used as a complementary material for 4D printed polylactic acid (PLA) structures to enhance their shape and force recovery properties and lower the stimulation temperature for more practical implementations. Two approaches are followed to provide SMP composites (SMPCs): multi-layered and multi-material lattices. In multi-layered lattices, specimens are comprised of separate layers and different ratios of SMP and TPE materials. For comparison, PLA-TPE filaments with the same ratios of multi-layered lattices are produced and used to fabricate multi-material lattices. Dynamic mechanical thermal analysis tests showed a reduction in the glass transition temperature of the manufactured PLA-TPE filament. X-ray diffraction test was conducted to prove that the crystallinity of the developed PLA-TPE material increases which explains the better shape memory effect in the multi-material specimens. Phase separation occurred in low ratios of TPE in PLA, discernible in field emission scanning electron microscope (FESEM) images, resultting in low quality in one of the developed PLA-TPE filaments. FESEM images also showed proper miscibility of TPE in PLA in higher ratios. Thermomechanical tests were done on printed specimens to examine and compare the shape and force recovery of the produced SMPCs. While the shape recovery of multi-material samples was not as good as multi-layered samples, both approaches have better shape recovery results than the PLA sample. Due to a lower glass transition temperature in multi-material lattices, their shape recovery process started at lower temperatures widening their potential practical applications. Force recovery of multi-material samples revealed a significant improvement which was due to more oriented crystalline polymer structures.