Influence of tempering temperature on the fretting wear of low alloyed martensitic construction steel

Journal article (2020)

Authors

Qibing Tang Southwest Jiaotong University

Xuejiao Wei Southwest Jiaotong University

Hao Li Southwest Jiaotong University

Xinyue Qiu Southwest Jiaotong University

Xiaojun Xu Southwest Jiaotong University

Guoqing Gou Southwest Jiaotong University

W. Xu Northeastern University China, Novel Aerospace Materials - Aerospace Engineering

Minhao Zhu Southwest Jiaotong University

Research Group

Novel Aerospace Materials (Aerospace Engineering) (TU Delft)

Microstructure Failure mechanism Tempering Fretting wear Martensitic steel

To reference this document use:

http://resolver.tudelft.nl/uuid:19067698-2c90-4258-9e38-abae286eb086

More Info

expand_more

Published Date

2020

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Aerospace Engineering

Department

Aerospace Structures & Materials

Research Group

Novel Aerospace Materials

Abstract

An experimental investigation was conducted to study the fretting wear behavior of low alloyed construction steel in the tempered fully martensitic state. The resulting damage mechanism and the resistance to fretting wear of martensitic steels subjected to different tempering temperature was evaluated and compared with the virgin (un-tempered) martensitic steel under the different loading conditions. The results show that the friction coefficient increases with the increase of the tempering temperature for all the applied loads. The fretting wear resistance mainly depends on the tempering temperature. Compared to the virgin (un-tempered) full martensite, most of the tempered martensites have better fretting wear resistance, in which the tempered martensitic (TM) steel of 200° due to a good balance of strength and ductility has a super fretting wear resistance for all loading conditions. In addition, the correlation of fretting wear resistance with the initial hardness was discussed.